진동기구의 SAE 5155강재 부식에 따른 압축 잔류응력의 영향

• 영문명: The Effects of Compressive Residual Stress by Corrosion a SAE5155 Steel Vibrating Apparatus
• 발행기관: 한국산업기술융합학회(구. 산업기술교육훈련학회)
• 저자명: 박재정(Jae Jung Park)
• 간행물 정보: 『산업기술연구논문지』산업기술교육훈련논문지 제20권 3호, 111~118쪽, 전체 8쪽
• 주제분류: 공학 > 공학일반
• 파일형태: PDF
• 발행일자: 2015.09.30

영문 초록

A study of corrosive environment under shot peening processing, compressive residual stress formed within materials interacts with growth stress due to corrosion progress. This causes long time of protective coating formation and subsequent higher resistance of corrosion than un peening materials. Corrosion fatigue crack growth rate in each corrosive solution as a whole was lower for shot peening than un peening. This is regarded that the compressive residual stress acts as harness and slows down fatigue crack growth rate. Threshold stress intensity factor in the corrosive environment was lower under corrosive environment than at room temperature. This is regarded that in the range of low frequency stress intensity factor at the crack tip acts as a partial electrochemical corrosion and the growth of fatigue crack progress rate shows a low value. Fatigue life at room temperature is 453 percent higher for shot peening specimen than un peening specimen. The percentage was 294, 488 366 higher under corrosive environment of 6% FeCl3 solution, 10% HNO3 + 3% HF solution, 3.5% NaCl in aqueous solution respectively. The results indicate shot peening effects is high for critical corrosion.

목차

ABSTRACT

Ⅰ. 서론

Ⅱ. 시험편 및 실험방법

Ⅲ. 실험결과 및 고찰

Ⅳ. 결론

참고문헌

키워드

압축잔류응력 쇼트피닝 피로수명 Compressive Residual Stress Shot Peening Fatigue Life