철계 소결합금의 내마모 특성에 미치는 미소기공의 영향

• 영문명: Effects of Micro Porosity on the Wear Characteristic of Sintered Alloy
• 발행기관: 한국산업기술융합학회(구. 산업기술교육훈련학회)
• 저자명: 송재형(Jae-Hyung Song)
• 간행물 정보: 『산업기술연구논문지』산업기술교육훈련논문지 제17권 4호, 115~122쪽, 전체 8쪽
• 주제분류: 공학 > 공학일반
• 파일형태: PDF
• 발행일자: 2012.12.30

영문 초록

This research discusses the pin-on-disk test and the hardness test against the Fe-base low alloy powder sinter to automotive transmission materials must provide high and stable friction, low noise and vibration, and high wear resistance, under various conditions such as temperature, vehicle speed and pressure. To satisfy the above requirements, several different material ingredients are usually combined to form complex friction materials. find out the friction and wear characteristics, and the investigation on automotive transmission to establish the theoretical friction and wear characteristics. It was observed almost pearlite and Ni particle in sintered specimen and porosity which was characteristic of sintered alloy. Surface of the carburization specimen was mostly martensite that was included micro porosity. Tensile strength of sinter and carburization specimen was observed 592.5 MPa and 1173 MPa. In the case of impact energy was showed 28.4J and 17.7J respectively. Average friction coefficient of sintered was reduced largely compare with carburization specimen. Wear depth of sintered specimen was increased with load increment, but an amount of increment was trifled in the case of carburization. It was expected that was possible to improve friction and wear characteristics largely. Because of very micro porosity by making powder form delayed oil long time in lubrication condition.

목차

Ⅰ. 서 론

Ⅱ. 실험방법

Ⅲ. 실험 결과 및 고찰

Ⅳ. 결 론

키워드

Micro Porosity(미소기공) Characteristic(마모특성) Sintered Alloy(소결합금) Carburization(침탄)