방전 플라즈마 소결법의 공정특성이 Ni분말 소결체에 미치는 영향

• 영문명: Sintering Behavior of Ni Powder by Spark Plasma Sintering
• 발행기관: 한국산업기술융합학회(구. 산업기술교육훈련학회)
• 저자명: 김기엽(Gi-Yeob Kim)
• 간행물 정보: 『산업기술연구논문지』산업기술교육훈련논문지 제18권 3호, 183~188쪽, 전체 6쪽
• 주제분류: 공학 > 공학일반
• 파일형태: PDF
• 발행일자: 2013.09.30

영문 초록

The spark plasma sintering(SPS) process, that enables rapid sintering under the condition of lower temperature combined with pressure application in various environment, is proposed as a novel process of powder forming. The effects of various sintering conditions on the density of Ni powder compacts were investigated by observing the densification behavior and actual temperature of specimens, and the results are summarized as follows: The densification rate of powder compacts was very fast in spite of shorter process time(less than 10 min) compare to conventional sintering process. The relative density of sintered compact was 98 % when the powder compact was sintered at 800 ℃ for 1 min under 40 MPa pressure. The densification behavior was affected by heating rate of powder compacts, shape and size of raw powder. At 800 ℃ of die temperature, the temperature of specimen inside was 920 ℃.

목차

Ⅰ. 서 론

Ⅱ. 실험방법

Ⅲ. 결과 및 고찰

Ⅳ. 결 론

키워드

Spark Plasma Sintering 방전플라즈마 소결공법 Ni Powder 니켈 분말 Densification Behavior 조밀화 거동 Graphite Mold 흑연 주형 Pulsed Current 펄스 전류