Bonding Temperature Effects of Robust Ag Sinter Joints in Air without Pressure within 10 Minutes for Use in Power Module Packaging
이용수 5
- 영문명
- Bonding Temperature Effects of Robust Ag Sinter Joints in Air without Pressure within 10 Minutes for Use in Power Module Packaging
- 발행기관
- 한국마이크로전자및패키징학회
- 저자명
- 김동진 김서아 김민수
- 간행물 정보
- 『마이크로전자 및 패키징학회지』제29권 제4호, 41~47쪽, 전체 7쪽
- 주제분류
- 공학 > 산업공학
- 파일형태
- 발행일자
- 2022.12.31
4,000원
구매일시로부터 72시간 이내에 다운로드 가능합니다.
이 학술논문 정보는 (주)교보문고와 각 발행기관 사이에 저작물 이용 계약이 체결된 것으로, 교보문고를 통해 제공되고 있습니다.
국문 초록
영문 초록
Ag sintering technologies have received great attention as it was applied to the inverter of Tesla's electric vehicle Model III. Ag sinter bonding technology has advantages in heat dissipation design as well as high-temperature stability due to the intrinsic properties of the material, so it is useful for practical use of SiC and GaN devices. This study was carried out to understand the sinter joining temperature effect on the robust Ag sintered joints in air without pressure within 10 min. Electroplated Ag finished Cu dies (3 mm × 3 mm × 2 mm) and substrates (10 mm × 10 mm × 2 mm) were introduced, respectively, and nano Ag paste was applied as a bonding material. The sinter joining process was performed without pressure in air with the bonding temperature as a variable of 175 °C, 200 °C, 225 °C, and 250 °C. As results, the bonding temperature of 175 °C caused 13.21 MPa of die shear strength, and when the bonding temperature was raised to 200 °C, the bonding strength increased by 157% to 33.99 MPa. When the bonding temperature was increased to 225 °C, the bonding strength of 46.54 MPa increased by about 37% compared to that of 200 °C, and even at a bonding temperature of 250 °C, the bonding strength exceeded 50 MPa. The bonding strength of Ag sinter joints was directly influenced by changes in the necking thickness and interfacial connection ratio. In addition, developments in the morphologies of the joint interface and porous structure have a significant effect on displacement. This study is systematically discussed on the relationship between processing temperatures and bonding strength of Ag sinter joints.
목차
1. Introduction
2. Experimental Procedures
3. Results and Discussion
4. Conclusions
Acknowledgment
References
해당간행물 수록 논문
- 표면처리와 전극 재료가 철-니켈 합금 도금에 미치는 영향
- Flake-type Ag분말의 입자크기에 따른 신축성 전극 특성 연구
- PCB 구리 에칭 용액의 에칭 특성에 대한 전기화학적 고찰
- Bonding Temperature Effects of Robust Ag Sinter Joints in Air without Pressure within 10 Minutes for Use in Power Module Packaging
- 3D 패키징을 위한 Scallop-free TSV와 Cu Pillar 및 하이브리드 본딩
- O₂ 플라즈마 표면 처리 공정 후 라미네이션 공정으로 제작된 흑연 페이스트 기반의 저비용 및 고감도 유연 압력 센서
- 미세 유체 기반의 형광 다중 암 진단 센서 플랫폼 설계
- 통전활성소결법으로 제조한 VO₂의 금속-절연체 전이 특성에 W와 Mg 첨가가 미치는 영향
- 폴리이미드 가교로 기계적 강도가 향상된 실리카 기반 에어로겔의 합성 및 물리화학적 특성 분석
- 열전도도 저감 기반의 열전소재 성능 증대 전략 수립을 위한 수식적 이해
- 복수의 아민기를 가지는 전구체를 적용하여 기계적 강도를 향상시킨 폴리우레아 가교 실리카 에어로겔
- 위상지연 필름을 이용한 가시광 투과율 가변형 스마트윈도우 제작
- 유전 센서 및 광섬유 센서를 이용한 EMC 유효 경화 수축 측정
- RF Sputtering 방법으로 증착된 Zn0.85Mg0.15O 박막을 적용한 고효율 양자점 전계 발광 소자 연구
참고문헌
교보eBook 첫 방문을 환영 합니다!
신규가입 혜택 지급이 완료 되었습니다.
바로 사용 가능한 교보e캐시 1,000원 (유효기간 7일)
지금 바로 교보eBook의 다양한 콘텐츠를 이용해 보세요!