Thermo-electrical properties of randomly oriented carbon/carbon composite

• 영문명: Thermo-electrical properties of randomly oriented carbon/carbon composite
• 발행기관: 한국탄소학회
• 저자명: Thakur Sudesh Kumar Raunija,N. Supriya
• 간행물 정보: 『Carbon Letters』제22권, 25~35쪽, 전체 11쪽
• 주제분류: 자연과학 > 자연과학일반
• 파일형태: PDF
• 발행일자: 2017.04.01

영문 초록

The aim of the work was to investigate the thermo-electrical properties of low cost and rapidly produced randomly oriented carbon/carbon (C/C) composite. The composite body was fabricated by combining the high-pressure hot-pressing (HP) method with the lowpressure impregnation thermosetting carbonization (ITC) method. After the ITC method step selected samples were graphitized at 3000°C. Detailed characterization of the samples’ physical properties and thermal properties, including thermal diffusivity, thermal conductivity, specific heat and coefficient of thermal expansion, was carried out. Additionally, direct current (DC) electrical conductivity in both the in-plane and through-plane directions was evaluated. The results indicated that after graphitization the specimens had excellent carbon purity (99.9 %) as compared to that after carbonization (98.1). The results further showed an increasing trend in thermal conductivity with temperature for the carbonized samples and a decreasing trend in thermal conductivity with temperature for graphitized samples. The influence of the thickness of the test specimen on the thermal conductivity was found to be negligible. Further, all of the specimens after graphitization displayed an enormous increase in electrical conductivity (from 190 to 565 and 595 to 1180 S/cm in the through-plane and in-plane directions, respectively).

목차

1. Introduction

2. Experimental

3. Results and Discussion

4. Conclusions

References

키워드

Exfoliated carbon fibers, specific heat, thermal diffusivity,thermal conductivity,CTE