Activated carbons prepared from mixtures of coal tar pitch and petroleum pitch and their electrochemical performance as electrode materials for electric double-layer capacitor

• 영문명: Activated carbons prepared from mixtures of coal tar pitch and petroleum pitch and their electrochemical performance as electrode materials for electric double-layer capacitor
• 발행기관: 한국탄소학회
• 저자명: Eunji Lee Soon Hyung Kwon Poo Reum Choi Ji Chul Jung Myung-Soo Kim
• 간행물 정보: 『Carbon Letters』제16권 제2호, 78~85쪽, 전체 8쪽
• 주제분류: 자연과학 > 자연과학일반
• 파일형태: PDF
• 발행일자: 2015.04.30

영문 초록

Activated carbons (ACs) were prepared by activation of coal tar pitch (CTP) in the range of 700°C-1000°C for 1-4 h using potassium hydroxide (KOH) powder as the activation agent. The optimal activation conditions were determined to be a CTP/KOH ratio of 1:4, activation temperature of 900°C, and activation time of 3 h. The obtained ACs showed increased pore size distribution in the range of 1 to 2 nm and the highest specific capacitance of 122 F/g in a two-electrode system with an organic electrolyte, as measured by a charge-discharge method in the voltage range of 0-2.7 V. In order to improve the performance of the electric double-layer capacitor electrode, various mixtures of CTP and petroleum pitch (PP) were activated at the optimal activation conditions previously determined for CTP. Although the specific capacitance of AC electrodes prepared from CTP only and the mixtures of CTP and PP was not significantly different at a current density of 1 A/g, the AC electrodes from CTP and PP mixtures showed outstanding specific capacitance at higher current rates. In particular, CTP-PP61 (6:1 mixture) had the highest specific capacitance of 132 F/g, and the specific capacitance remained above 90% at a high current density of 3 A/g. It was found that the high specific capacitance could be attributed to the increased micro-pore volume of ACs with pore sizes from 1 to 2 nm, and the high power density could be attributed to the increased meso-pore volume.

목차

1. Introduction

2. Experimental

3. Results and Discussion

4. Conclusions

Acknowledgements

References

키워드

activated carbon pitch electric double-layer capacitor electrochemical properties