Optical spectroscopy of Tb³+ ions doped NaCa(PO₃)₃ phosphors

• 영문명: Tb³+ 이온이 첨가된 NaCa(PO₃)₃ 형광체의 형광특성
• 발행기관: 한국방사선학회
• 저자명: Changyong Yoon()
• 간행물 정보: 『한국방사선학회 논문지』 제12권 제4호, 451~457쪽, 전체 7쪽
• 주제분류: 공학 > 기타공학
• 파일형태: PDF
• 발행일자: 2018.08.30

국문 초록

Luminescence properties of NaCa(PO₃)₃ doped with Tb³+ ions are investigated by optical and laser excitation spectroscopy. The phosphors were prepared by solidstate reaction method The X-ray diffraction(XRD) was used to analyze the crystal structure and the crystallinity of the samples. The excitation and emission spectra and decay curve of NaCa(PO₃)₃ : Tb³+ (0.01~30mol%) were measured at room temperature. The f-d band of Tb³+ is observed in the excitation spectra of NaCa(PO₃)₃:Tb³ in the wave length region 205~245nm. Strong emission lines due to the 5 D₄→ 7 F J transition and weak emission lines due to the 5 D₄→ 7 F J transition are observed in the emission spectra of NaCa(PO₃)₃: Tb³+. The energy transfer and cross relaxation between Tb³+ ions are discussed in NaCa(PO₃)₃: Tb³+ in the emission spectra and life time.

영문 초록

Tb 3+ 이온이 첨가된 NaCa(PO₃)₃ 형광체의 여기 및 방출 스펙트럼 및 레이저 분광 측정을 통하여 형광특성을 조사 하였다. 고상법으로 NaCa(PO₃)₃:Tb³+ 형광체를 합성하였다. X선 회절측정(XRD)을 사용하여 형광체의 결정 구조 및 결정성을 분석하여 Tb³+ 이온이 30 mol%까지 첨가되어도 형광체의 결정구조가 NaCa(PO₃)₃의 결정상을 유지하였다. NaCa(PO₃)₃: Tb³+ (0.01-30mol %)형광체의 여기 및 방출 스펙트럼과 형광의 감쇠곡선을 상온에서 측정 하였다. NaCa(PO₃)₃ :Tb³+ 의 여기 스펙트럼에서 205~245 nm 영역에서 넓은 Tb³+ 의 4f-5d 전이에 의한 f-d 밴드가 나타났다. NaCa(PO₃)₃ :Tb³+ 의 방출 스펙트럼에서 5D₄→ 7 F J 전이에 의한 강한 피크와 5 D₃→ 7 F J 전이에 약한 피크가 관찰 되었다. 방출 스펙트럼의 형광 강도와 형광의 수명시간 분석을 통하여 Tb³+ 이온 사이의 에너지 전이 및 교차 이완이 확인되었다.

목차

Ⅰ. INTRODUCTION

Ⅱ. MATERIAL AND METHODS

Ⅲ. RESULTS

Ⅳ. DISCUSSION

Ⅴ. CONCLUSION

키워드

Luminescence X-ray diffraction Energy transfer 형광 X선 회절측정 에너지 전이